Reaction Products
與其它產(chǎn)品的化學反應(yīng)情況 |
|
| Silicones 硅硐膠： |
| Acetoxy 乙酸基 |
|
acetic acid 醋酸
* 有氣味 Smell
* 腐蝕 Corrosion
* 化學反應(yīng) chemical reaction
|
| Alkoxy 烷氧基 |
|
alcohol/methanol 酒精/甲醇
* 抑制聚氨酯的固化 curing inhibition of Polyurethane
* 有可能會影響某些涂漆的固化
Slight possibility on inhibiting curing of some paint systems. |
|
|
| Polyurethane 聚氨酯膠： |
| Traditionally cured systems 傳統(tǒng)固化系統(tǒng)： |
|
* 會產(chǎn)生二氧化碳 formation of CO2
* 在溫度/濕度很高/大的條件下有可能產(chǎn)生氣泡
Possible bubbling risk at increasing Tempreture/Humidity. |
|
|
|
Skinning time
成膜時間 |
|
|
| Silicones 硅硐膠： |
|
* 一般較短10 - 20 分鐘 Generally short 10 - 20 min.
* 特別在濕度高時，打膠短
Applicator can only make short runs especially at high humidity
* 需要立即平滑 Immediate smoothening required |
|
|
| Polyurethane 聚氨酯膠： |
|
* 施用者有更長的施工時間大約 2 - 4 小時
2 - 4 hours longer runs / more time for applicator
* 在高溫和高濕度的情況下， 打膠和刮平不太受影響
Application & smoothening time less effected even at high temperature and humidity |
|
|
|
Resistance to solvent / gasoline
抗溶劑及汽油 |
|
|
| Silicones 硅硐膠： |
|
* 不宜與溶劑/汽油/燃油接觸
Not suitable in contact with solvents/ gasoline/ fuel
溶劑的吸收性 Absorption of solvents
* 有氣味 swelling
* 性能的消失 loss of properties |
|
|
| Polyurethane 聚氨酯膠： |
|
* 很好的抗溶劑侵蝕性 very good resistance to solvents
* 可在儲存區(qū)/汽油站等地方使用 use in storage areas / gasoline stations etc. |
|
|